Kjellberg Finsterwalde Plasma und Maschinen GmbH焊条
德国Kjellberg Finsterwalde Plasma und Maschinen GmbH焊条
产品系列:
- Unalloyed Electrodes 非合金电极
- High-Temperature Electrodes 高温电极
- Stainless Electrodes 不锈钢焊条
- Nickel-Base Alloys 镍基合金
- Cast Iron Electrodes 铸铁焊条
- Surfacing Electrodes 堆焊焊条
- Cutting Electrodes 切割电极
|
Unalloyed Welding Electrodes
according to DIN EN ISO 2560-A, DIN 1913 and AWS A 5.1
|
LLOYD
Rutile-coated stick electrode for shipbuilding
|
LLOYD GRUEN
Rutile-cellulosic-coated stick electrode for shipbuilding
|
PRIMA
Rutile-cellulosic-coated general purpose electrode for all positions
|
PRIMA S
Thick coated rutile-cellulose general purpose welding electrode
|
PRIMA BLUE
Rutile-cellulosic coated welding rod for all welding positions
|
PERFEKT
Basic-coated stick electrode for welding in vertical down position
|
TITAN ROT
Heavy rutile-coated general purpose welding electrode
|
TITAN S
Heavy rutile-coated general purpose welding electrode with high strength and thoughness
|
TITAN
Rutile-basic-coated general purpose welding electrode
|
TITAN K
Rutile-basic-coated welding electrode with high strength and thoughness
|
OPTIMAL
Rutile-basic-coated stick electrode for thin sheet thickness
|
KONTAKT 160
Heavy rutile-coated stick electrode with high recovery
|
TRUMPF
Acid-coated special electrode
|
PROGRESS
Basic-coated stick electrode for welding in vertical up position
|
GARANT
Basic-coated general purpose welding electrode
|
GARANT S
Basic-coated general purpose welding electrode with high strength
|
GARANT K
Basic-coated, nickel alloy stick electrode with high strength and thoughness, low hydrogen content
|
GARANT BR
Double rutile-basic-coated welding electrode
|
GARANT AC/DC
Rutile-basic-coated stick electrode with high strength
|
High-Temperature Welding Electrodes
according to DIN EN 1599, DIN 8575 and AWS A 5.5
|
KOMPLEX W
Stick electrode including 0.5% Mo for welds of identical and similar steels (e.g. 16Mo3), rutile-coated
|
IMPULS
Stick electrode including 0.6% Ni and 0.4% Mo for welds of identical and similar steels, basic-coated
|
MOB
Stick electrode including 0.5% Mo for welds of identical and similar steels (e.g. 16Mo3), basic-coated
|
CROMO 1R
Stick electrode including 1% Cr and 0.5% Mo for welds of identical and similar steels (e.g. 13CrMo4-5), rutile-coated
|
CROMO 1B
Stick electrode including 1% Cr and 0.5% Mo for welds of identical and similar steels (e.g. 13CrMo4-5), basic-coated
|
CROMO 2B
Stick electrode including 2,2% Cr and 1% Mo for welds of identical and similar steels (e.g. 10CrMo9-10), basic-coated
|
High-alloyed Welding Electrodes
according to DIN EN 1600 and DIN 8556
|
FINOX 4820 AC
Rod electrode 26% Cr, 4% Ni, material number 1.4820
|
FINOX 4842 AC
Rod electrode with 26% Cr, 20% Ni, material number 1.4842, AWS 310
|
Finox 4842 B
Rod electrode with 26% CR, 20% Ni, material number 1.4842, AWS 310, basic-coated
|
FINOX 4829 AC
Rod electrode with 22% CR, 12% Ni, material number 1.4829, AWS 309
|
FINOX 4316 AC
Rod electrode with 19% Cr, 9% Ni, material number 1.4316, AWS 308L
|
FINOX 4551 AC
Niobium-stabilised rod electrode with 19% Cr, 9% Ni, material number 1.4551, AWS 347
|
FINOX 4551 B
Niobium-stabilised rod electrode with 19% Cr, 9% Ni, material number 1.4551, AWS 347, with higher toughness, basic-coated
|
Finox 4430 AC
Rod electrode with 19% Cr, 12% Ni, 3% Mo, material number 1.4430, AWS 316L
|
FINOX 4430 F
Special electrode for vertical down welding with 19% Cr, 12% Ni, 3% Mo, material number 1.4430, AWS 316L
|
FINOX 4576 AC
Niobium-stabilised rod electrode with 19% Cr, 12% Ni, 3% Mo, material number 1.4576, AWS 318
|
FINOX 4462 AC
Special electrode for duplex-steels of the alloy 22% Cr, 9% Ni, 3% Mo, material number 1.4462, AWS 2209
|
FINOX 4519 AC
Rod electrode with 20% Cr, 25% Ni, 5% Mo and copper, material number 1.4519, AWS 385
|
FINOX 4370 AC
Electrode for black-and-white joints, also for hard-manganese steel with 18% Cr, 8% Ni, 6% Mn, material number 1.4370, AWS 307
|
FINOX 4431 AC
Electrode for black-and-white joints, also for hard-manganese steel with 20% Cr, 10% Ni, 3% Mo, material number 1.4431, AWS 308Mo
|
FINOX 4337 AC
Black-and-white general purpose electrode with 29% Cr, 9% Ni, material number 1.4337, AWS 312
|
FINOX 4332 AC
Electrode for black-and-white joints with 23% Cr, 13% Ni, material number 1.4332, AWS 309L
|
FINOX 4459 AC
Electrode for black-and-white joints with 23% Cr, 13% Ni, 2% Mo, material number 1.4459, AWS 309MoL
|
FINOX 29/9 GOLD
Special electrode for or extremely crack-resistant joint welding with 30% Cr, 9.5% Ni, 1% Mn, Material number 1.4337, AWS E312-16
|
Nickel-Base Alloy Electrodes
according to DIN EN ISO 14172 and AWS A 5.11
|
FINOX 182
Nickel-base electrode of the alloy class 182 (nickel-chromium-iron)
|
FINOX 625
Nickel-base electrode of the alloy class 625 (nickel-chromium-molybdenum)
|
Cast Iron Welding Electrodes
according to DIN EN ISO 1071, DIN 8573 and AWS A 5.15
|
FINCAST NI
Nickel electrode for cold welding of grey cast iron
|
FINCAST NIFE
Nickel-ferrum electrode for cold welding of grey cast iron (GGL and GGG types), malleable and spheroidal cast iron
|
FINCAST NIFE K
Special electrode with copper-plated nickel-ferrum core rod for cold welding of grey cast iron (GGL and GGG types), malleable and spheroidal cast iron
|
FICAST FE
Special purpose welding rod for buffering layers and single layer surfacings on scaled and corroded iron castings
|
Surfacing Electrodes
according to DIN EN 14700 and DIN 8555
|
FIDUR 1/300
Surfacing electrode, Mo- and V-alloyed, hardness 300 HB, surfacing on components with sliding wear
|
FIDUR 2/55
Surfacing electrode for hard and tough layers on unalloyed and low-alloyed steel, good edge-holding properties, hardness 55 HRC
|
FIDUR 3/50
Surfacing electrode for hot and cold working tools, hardness 50 HRC
|
FIDUR 4/60
Surfacing electrode for high-speed tools, hardness 60 HRC
|
FIDUR 6/55
Surfacing electrode for tough-hard, abrasion-proof layers on unalloyed and low-alloyed steel, hardness 55 HRC
|
FIDUR 6/60
Surfacing electrode for tough-hard, abrasion-proof surfacing layers, hardness 60 HRC
|
FIDUR 6/60 R
Rutile-coated surfacing electrode for tough -ard, abrasion-resistant layers, hardness 60 HRC, suitable for AC current
|
FIDUR 7/200
Surfacing electrode for crack-resistant stainless layers on hard-manganese steel, hardness 200 HB, work-hardenable
|
FIDUR 8/200
Surfacing electrode for railways and hard-manganese steel, hardness 200 HB, stainless, work-hardenable
|
FIDUR 10/60
Surfacing electrode for highly wear-resistant stainless layers which are exposed to abrasive and grinding wear, hardness 60 HRC, 160% recovery
|
FIDUR 10/65
Surfacing electrode for highly abrasive-resistant stainless layers which are exposed to strong abrasive and grinding wear and high temperatures, hardness 65 HRC, 190% recovery
|
FIDUR 10/70
Surfacing electrode for wear-resistant, stainless layers which are exposed to heavy abrasive and grinding wear and also high temperatures, hardness 70 HRC, 240% recovery
|
FILIT 6
Cobalt-base surfacing electrode, resistant against cavitation, erosion, corrosion, good thermal-shock resistance, hardness 40 HRC
|
FIDUR 23/250
Nickel-base surfacing electrode of alloy class 275 (nickel-chromiu-molybdenum), good thermal-shock resistance
|
MET-OX
Coated cutting electrode
|
KJELGOUGE
Coated gouging electrode
|
|